Nickel Alloy Pipes

Characteristics Mechanical

MATERIALS
MECHANICAL CHARACTERISTICS
Grade
UNS
W.N.
ASTM Plates
P.S. Density kg/dm3
Tensile strenght min N/mm2
Yeld point min N/mm2
Elongation 2" min %
Hardness max HB
Hardness max HRB
ALLOY 600
N06600
2.4816
B168
8,4
550
240
30
180
90
ALLOY 601
N06601
2.4851
B168
8,1
550
205
30
180
90
ALLOY 625
N06625
2.4856
B443
8,5
758
379
30
-
-
ALLOY 800H
N08810
1.4958
B409
8,0
450
170
30
-
-
ALLOY 800HT
N08811
1.4959
B409
8,0
450
170
30
-
-
ALLOY 825
N08825
2.4858
B424
8,1
586
241
30
165
87
ALLOY B2
N10665
2.4617
B333
9,2
760
350
40
226
100
ALLOY B3
N10675
2.46
B333
9,2
760
350
40
226
100
ALLOY B4
N10629
2.46
B333
9,2
760
350
40
-
100
ALLOY C22
N06022
2.4602
B575
8,7
690
310
45
-
100
ALLOY 59
N06059
2.4605
B575
8,8
710
350
45
-
100
ALLOY C276
N10276
2.4819
B575
8,9
690
283
40
226
100
ALLOY C4
N06455
2.461
B575
8,
690
276
40
226
100
ALLOY X
N06002
2.4665
B435
8,3
655
240
35
-
-
ALLOY G30
N06030
2.4603
B582
8,2
586
241
30
-
-
Cu Ni 90/10
C70600
2.0872
B171
8,9
275
105
30
-
-

Chemical Analysis

MAT.
CHEMICAL ANALYSIS
Den.
C % max
Mn %  max
Si % max
P % max
S %  max
Cr
Ni
Mo
Fe
Cu
Co
Al
others elements
NICKEL 200
0,15
0,35
0,35
-
0,010
-
98,4 ÷99,6
-
0,40 max
0,25 max
-
-
-
NICKEL 201
0,01
0,35
0,35
-
0,010
-
98,4 ÷ 99,6
-
0,40 max
0,25 max
-
-
-
ALLOY 400
0,30
2,00
0,50
-
0,024
-
63 min
-
2,50 max
28÷34
-
-
-
ALLOY 600
0,15
1,00
0,50
-
0,015
14÷17
72 min
-
6÷10
0,50 max
-
-
-
ALLOY 601
0,10
1,05
0,50
-
0,015
21÷25
58÷63
-
-
1,00 max
-
1÷1,7
-
ALLOY 625
0,10
0,50
0,50
0,015
0,015
20÷23
58min
8÷10
5,0 max
-
-
0,40 max
-
ALLOY 800H
0,05 ÷0,1
1,50
1,00
-
0,015
19÷23
30÷35
-
39,5 min
0,75 max
-
0,15 ÷0,6
-
ALLOY 800HT
0,06 ÷0,5
1,50
1,00
-
0,015
19÷23
30÷35
-
39,5 min
0,75 max
-
0,15 ÷0,6
-
ALLOY 825
0,05
1,00
0,50
-
0,030
19,5 ÷23,5
38÷46
2,5 ÷ 3,5
22 min
1,5÷3
-
0,2 max
-
ALLOY B2
0,02
1,00
0,10
0,040
0,030
1,00 max
balance
26÷30
2,00 max
-
1,00 max
-
-
ALLOY B3
0,01
3,00
0,10
0,030
0,010
1÷3
balance
27÷32
1÷3
0,2 max
3max
0,5 max
ALLOY B4
0,01
1,50
0,05
0,04
0,010
0,5÷1,5
balance
26÷30
1÷6
0,5
2,5
0,1÷0,5
-
ALLOY C22
0,015
0,50
0,08
0,020
0,020
20 ÷22,5
balance
12,5 ÷14,5
2÷6
-
-
-
-
ALLOY 59
0,010
0,50
0,10
0,015
0,005
22÷24
balance
16,5
1,5
-
0,3 max
0,1 ÷0,4
-
ALLOY C276
0,01
1,00
0,08
0,040
0,030
14,5 ÷16,5
balance
15÷17
4÷7
-
2,50 max
-
-
ALLOY C4
0,015
1,00
0,08
0,040
0,030
14÷18
balance
14÷17
3,00
-
2,0
-
-
ALLOY X
0,05 ÷0,15
1,00
1,00
0,040
0,030
20,5 ÷23
balance
8÷10
17÷20
-
0,5 ÷2,5
-
-
ALLOY G30
0,03
1,50
0,80
0,040
0,020
28 ÷31,5
balance
4÷6
13
1,0
5 max
-
-
÷17
÷2,4
Cu Ni 90/10
0,05
1,00
-
0,020
0,020
-
11
-
1÷1,8
balance
-
-
-

The Specification covers alloys UNS NO8904, UNS NO8925, UNS NO8031, UNS NO8932, UNS NO8926 and UNS R20033 plate, sheet and strip in the annealed temper.

CHEMICAL REQUIREMENTS

Element
Composition, % UNS N08904
Composition, % UNS N08925
Composition, % UNS N08932
Composition, % UNS N08031
Composition, % UNS N08926
Composition, % UNS R20033
Carbon, max
0.020
0.020
0.020
0.015
0.020
0.015
Manganese, max
2.00
1.00
2.00
2.0
2.00
2.0
Phosphorus, max
0.045
0.045
0.025
0.020
0.03
0.02
Sulphur, max
0.035
0.030
0.010
0.010
0.01
0.01
Silicon, max
1.00
0.50
0.40
0.3
0.5
0.50
Nickel
23.00 - 28.00
24.00 - 26.00
24.0 - 26.0
30.0 - 32.0
24.00 - 26.00
30.0 - 33.0
Chromium
19.00 - 23.00
19.00 - 21.00
24.0 - 26.0
26.0 - 28.0
19.00 - 21.00
31.0 - 35.0
Molybdenum
4.0 - 5.0
6.0 - 7.0
4.5 - 6.5
6.0 - 7.0
6.0 - 7.0
0.50 - 2.0
Copper
1.0 - 2.0
0.8 - 1.5
1.0 - 2.0
1.0 - 1.4
0.5 - 1.5
0.30 - 1.20
Nitrogen
...
0.10 - 0.20
0.15 - 0.25
0.15 - 0.25
0.15 - 0.25
0.35 - 0.60
Iron
balance
balance
balance
balance
balance
balance

PHYSICAL REQUIREMENTS

Alloy
Form
Tensile Strength, min, ksi (MPa)
Yield Strength (0.2% offset), min, psi (MPa)
Elongation in 2 in. or 50.8 min, or 4D, min, %
Rockwell Hardness (or equivalent)A
UNS N08904 Sheet
71 (490)
31 000 (215)
35
70-90 HRB
  Strip
71 (490)
31 000 (215)
35
70-90 HRB
  Plate
71 (490)
31 000 (215)
35
70-90 HRB
UNS N08925 Sheet
87 (600)
43 000 (295)
40
---
  Strip
87 (600)
43 000 (295)
40
---
  Plate
87 (600)
43 000 (295)
40
---
UNS N08932 Plate
87 (600)
44 000 (305)
40
---
UNS N08031 Sheet
94 (650)
40 000 (276)
40
---
  Strip
94 (650)
40 000 (276)
40
---
  Plate
94 (650)
40 000 (276)
40
---
UNS N08926 Sheet
94 (650)
43 000 (295)
35
---
  Strip
94 (650)
43 000 (295)
35
---
  Plate
94 (650)
43 000 (295)
35
---
UNS R20033 Sheet
109 (750)
55 000 (380)
40
---
  Strip
109 (750)
55 000 (380)
40
---
  Plate
109 (750)
55 000 (380)
40
---

A Hardness values are shown for information only and shall not constitute a basis for acceptance or rejection as long as the other mechanical properties are met.